PC PC 740/4 UV CC1320-08LG ALBIS PLASTIC GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ALBIS PLASTIC GmbH/ PC 740/4 UV CC1320-08LG |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 无断裂 |
| -20°C | ISO 179/1eU | 无断裂 | |
| Charpy Notched Impact Strength | -20°C | ISO 179/1eA | 12 kJ/m² |
| -- | ISO 179/1eA | 12 kJ/m² | |
| -40°C | ISO 179/1eA | 12 kJ/m² | |
| Impact strength of simply supported beam without notch | -- | ISO 179/1eU | 无断裂 |
| Supplementary Information | Test Condition | Test Method | ALBIS PLASTIC GmbH/ PC 740/4 UV CC1320-08LG |
|---|---|---|---|
| half-power angle | 3.00mm | 10.0 ° | |
| 4.00mm | 11.0 ° | ||
| 2.00mm | 8.00 ° | ||
| 1.00mm | 3.00 ° |
| Mechanical properties | Test Condition | Test Method | ALBIS PLASTIC GmbH/ PC 740/4 UV CC1320-08LG |
|---|---|---|---|
| FlexuralDeflectionMaxForce | ISO 178 | 7.0 % | |
| tensile strength | -- | ISO 527-2 | 66.0 MPa |
| Tensile modulus | ISO 527-2 | 2400 MPa | |
| Tensile strain | 断裂 | ISO 527-2 | 70 % |
| bending strength | 3.5%应变 | ISO 178 | 76.0 MPa |
| Tensile strain | 屈服 | ISO 527-2 | 6.0 % |
| tensile strength | 屈服 | ISO 527-2 | 66.0 MPa |
| bending strength | -- | ISO 178 | 100 MPa |
| Flexural modulus | ISO 178 | 2450 MPa |
| optical performance | Test Condition | Test Method | ALBIS PLASTIC GmbH/ PC 740/4 UV CC1320-08LG |
|---|---|---|---|
| transmissivity | 总计,2000µm | ISO 13468 | 88.7 % |
| Haze ratio | 4000µm2 | ISO 13468 | 93 % |
| 2000µm2 | ISO 13468 | 92 % | |
| 3000µm2 | ISO 13468 | 92 % | |
| transmissivity | 总计,3000µm | ISO 13468 | 88.5 % |
| 总计,1000µm | ISO 13468 | 89.5 % | |
| 总计,4000µm | ISO 13468 | 88.0 % | |
| Haze ratio | 1000µm3 | ISO 13468 | 79 % |
| flammability | Test Condition | Test Method | ALBIS PLASTIC GmbH/ PC 740/4 UV CC1320-08LG |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 850 °C |
| FireBehavior,FMVSS | 1.00mm | ISO 37 | passed |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 850 °C |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 850 °C |
| 4.0mm | IEC 60695-2-12 | 850 °C |
| physical property | Test Condition | Test Method | ALBIS PLASTIC GmbH/ PC 740/4 UV CC1320-08LG |
|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 20.0 cm³/10min |
| density | ISO 1183 | 1.20 g/cm³ |
| Thermal performance | Test Condition | Test Method | ALBIS PLASTIC GmbH/ PC 740/4 UV CC1320-08LG |
|---|---|---|---|
| vicat | ISO 306/B50 | 142 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 124 °C |