PBT+ASA Ultradur® S 4090 G6 BASF GERMANY

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.47 g/cm³
density	density		ISO 1183	1.47 g/cm³
Melt volume flow rate	275°C/2.16kg	ISO 1133	20.0 cm³/10min
Shrinkage rate	MD：3.18mm		0.30 %
	Shrinkage rate	TD	ISO 294-4	0.75 %
	Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.29 %
Water absorption rate	Saturation	ASTM D570	0.40 %
	Water absorption rate	饱和,23°C	ISO 62	0.40 %
		Water absorption rate	平衡,50%RH	ASTM D570	0.20 %
		Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.20 %
Viscosity value	降低的粘度	ISO 1628	105.0 ml/g

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	0.69mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile strain	断裂,23°C	ISO 527-2	2.2 %
	Tensile strain	断裂,80°C	ISO 527-2	3.6 %
		Tensile strain	断裂,120°C	ISO 527-2	5.9 %
		Tensile strain	Tensile strain	断裂,150°C	ISO 527-2	4.8 %
Tensile creep modulus	1hr	ISO 899-1	7600 MPa
tensile strength	断裂,80°C	ISO 527-2	79.0 MPa
	tensile strength	断裂,120°C	ISO 527-2	47.0 MPa
	tensile strength	tensile strength	断裂,150°C	ISO 527-2	35.0 MPa
elongation	断裂,23°C	ASTM D638	2.2 %
Tensile strain	断裂,-40°C	ISO 527-2	2.4 %
bending strength	23°C	ASTM D790	194 MPa
Tensile modulus	23°C	ISO 527-2	9700 MPa
tensile strength	断裂,23°C	ASTM D638	125 MPa
	tensile strength	断裂,-40°C	ISO 527-2	195 MPa
	tensile strength	tensile strength	断裂,23°C	ISO 527-2	125 MPa
Tensile creep modulus	1000hr	ISO 899-1	6700 MPa
Flexural modulus	23°C	ASTM D790	8270 MPa
Flexural modulus	Flexural modulus	23°C	ISO 178	8300 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23°C	ISO 179	9.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	50 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	59 kJ/m²
Impact strength of cantilever beam gap	-40°C	ASTM D256	69 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	85 J/m

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
dielectric constant	100Hz	IEC 60250	3.80
dielectric constant	dielectric constant	1MHz	IEC 60250	3.70
Dissipation Factor	100Hz	IEC 60250	3E-03
Dissipation Factor	Dissipation Factor	1MHz	IEC 60250	0.018
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 1
Surface Resistivity		ASTM D257	1E+14 ohms
Surface Resistivity	Surface Resistivity		IEC 60093	1E+14 ohms
Volume resistivity	1.50mm	ASTM D257	>1.0E+13 ohms·cm
Volume resistivity	Volume resistivity		IEC 60093	>1.0E+13 ohms·cm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火，HDT	ASTM D648	210 °C
RTI Elec	1.5mm	UL 746	130 °C
RTI Elec	RTI Elec	3.0mm	UL 746	130 °C
Heat distortion temperature	0.45MPa,未退火，HDT	ISO 75-2/B	210 °C
	Heat distortion temperature	1.8MPa,未退火，HDT	ASTM D648	177 °C
	Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火，HDT	ISO 75-2/A	175 °C
melting temperature		ASTM D3418	223 °C
melting temperature	melting temperature		ISO 3146	223 °C
Linear coefficient of thermal expansion	MD		4E-05 cm/cm/°C
RTI Elec	0.69mm	UL 746	130 °C
RTI Imp	1.5mm	UL 746	90.0 °C
RTI Imp	RTI Imp	3.0mm	UL 746	90.0 °C
RTI Str	0.69mm	UL 746	130 °C
	RTI Str	1.5mm	UL 746	130 °C
	RTI Str	RTI Str	3.0mm	UL 746	130 °C
RTI Imp	0.69mm	UL 746	90.0 °C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.