PBT+ASA Ultradur® S 4090 G6 BASF GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/Ultradur® S 4090 G6 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 69 J/m |
| 23°C | ASTM D256 | 85 J/m | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 50 kJ/m² |
| 23°C | ISO 179 | 59 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/Ultradur® S 4090 G6 |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 194 MPa |
| tensile strength | 断裂,23°C | ASTM D638 | 125 MPa |
| 断裂,120°C | ISO 527-2 | 47.0 MPa | |
| Tensile modulus | 23°C | ISO 527-2 | 9700 MPa |
| Tensile strain | 断裂,80°C | ISO 527-2 | 3.6 % |
| 断裂,150°C | ISO 527-2 | 4.8 % | |
| 断裂,-40°C | ISO 527-2 | 2.4 % | |
| Flexural modulus | 23°C | ISO 178 | 8300 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.2 % |
| tensile strength | 断裂,80°C | ISO 527-2 | 79.0 MPa |
| Tensile strain | 断裂,120°C | ISO 527-2 | 5.9 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 7600 MPa |
| tensile strength | 断裂,150°C | ISO 527-2 | 35.0 MPa |
| 断裂,23°C | ISO 527-2 | 125 MPa | |
| Flexural modulus | 23°C | ASTM D790 | 8270 MPa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 6700 MPa |
| tensile strength | 断裂,-40°C | ISO 527-2 | 195 MPa |
| elongation | 断裂,23°C | ASTM D638 | 2.2 % |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/Ultradur® S 4090 G6 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| dielectric constant | 100Hz | IEC 60250 | 3.80 |
| Surface Resistivity | ASTM D257 | 1E+14 ohms | |
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 3E-03 |
| Volume resistivity | 1.50mm | ASTM D257 | >1.0E+13 ohms·cm |
| dielectric constant | 1MHz | IEC 60250 | 3.70 |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.018 |
| flammability | Test Condition | Test Method | BASF GERMANY/Ultradur® S 4090 G6 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 0.69mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | BASF GERMANY/Ultradur® S 4090 G6 |
|---|---|---|---|
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 20.0 cm³/10min |
| Shrinkage rate | MD：3.18mm | 0.30 % | |
| TD | ISO 294-4 | 0.75 % | |
| Water absorption rate | 饱和 | ASTM D570 | 0.40 % |
| Shrinkage rate | MD | ISO 294-4 | 0.29 % |
| Water absorption rate | 平衡,50%RH | ASTM D570 | 0.20 % |
| 平衡,23°C,50%RH | ISO 62 | 0.20 % | |
| 饱和,23°C | ISO 62 | 0.40 % | |
| density | ASTM D792 | 1.47 g/cm³ | |
| ISO 1183 | 1.47 g/cm³ | ||
| Viscosity value | 降低的粘度 | ISO 1628 | 105.0 ml/g |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/Ultradur® S 4090 G6 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 177 °C |
| RTI Elec | 0.69mm | UL 746 | 130 °C |
| RTI Imp | 1.5mm | UL 746 | 90.0 °C |
| RTI Str | 0.69mm | UL 746 | 130 °C |
| melting temperature | ASTM D3418 | 223 °C | |
| RTI Imp | 0.69mm | UL 746 | 90.0 °C |
| RTI Elec | 3.0mm | UL 746 | 130 °C |
| RTI Imp | 3.0mm | UL 746 | 90.0 °C |
| melting temperature | ISO 3146 | 223 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 210 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 210 °C | |
| Linear coefficient of thermal expansion | MD | 4E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 175 °C |
| RTI Str | 1.5mm | UL 746 | 130 °C |
| 3.0mm | UL 746 | 130 °C | |
| RTI Elec | 1.5mm | UL 746 | 130 °C |