PA66 G4000HS1L NC01 INVISTA USA

ویژگی‌ها:
Glass fiber reinforced material 40%
filler
good dimensional stability
high tensile strength
thermal stability
and good demolding performance
مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 1183	1.47 g/cm³
Shrinkage rate	TD : 2.00 mm	ISO 294-4	0.85to0.95 %
Shrinkage rate	Shrinkage rate	MD : 2.00 mm	0.35到0.45	%
Water absorption rate	平衡, 23°C, 50% RH		1.1
Water absorption rate	Water absorption rate	23℃, 24 hr	ISO 62	0.70 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Thermal performance	热变形温度	ISO 527-2/B	260 0.45 MPa, 未退火
Thermal performance	Thermal performance	1.8 MPa, 未退火	ISO 527-2/A	250 ℃
melting temperature		ISO 11357-3	262 ℃
Tensile modulus		ISO 527-2	12300 MPa
tensile strength	Break	ISO 527-2	225 MPa
Tensile strain	Break	ISO 527-2	3.0 %
Flexural modulus		ISO 178	10300 MPa
bending strength		ISO 178	320 MPa
Charpy Notched Impact Strength	-40℃	ISO 179	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃		13
Impact strength of simply supported beam without notch	23℃	ISO 180	13 kJ/m²