برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.16 g/cm³ |
| density | | ISO 1183 | 1.16 g/cm³ |
| Melt volume flow rate | 275°C/5.0kg | ISO 1133 | 140 cm3/10min |
| Shrinkage rate | MD：3.18mm | | 0.80 % |
| Water absorption rate | 饱和 | ASTM D570 | 8.5 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 8.5 % |
| Water absorption rate | 平衡,50%RH | ASTM D570 | 2.9 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.9 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ball-indentation hardness | | ISO 2039-1 | 100 Mpa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.38mm | UL 94 | V-0 |
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服,23°C | ISO 527-2 | 75.0 Mpa |
| elongation | 屈服,23°C | ASTM D638 | 5.0 % |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.0 % |
| elongation | 断裂,23°C | ASTM D638 | 50 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 6.0 % |
| Flexural modulus | 23°C | ASTM D790 | 3000 Mpa |
| Flexural modulus | 23°C | ISO 178 | 3000 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 3500 Mpa |
| tensile strength | 屈服,23°C | ASTM D638 | 83.0 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179 | 4.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 80 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 32 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 43 J/m |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 4.5 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | 1.50mm | ASTM D257 | 1E+13 ohms·cm |
| Volume resistivity | | IEC 60093 | 1E+13 ohms·cm |
| dielectric strength | | IEC 60243-1 | 32 KV/mm |
| dielectric constant | 1MHz | IEC 60250 | 3.60 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD | | 8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | | 9E-05 cm/cm/°C |
| RTI Elec | 0.38mm | UL 746 | 110 °C |
| RTI Elec | 0.75mm | UL 746 | 120 °C |
| RTI Elec | 1.5mm | UL 746 | 120 °C |
| RTI Elec | 3.0mm | UL 746 | 120 °C |
| RTI Imp | 0.38mm | UL 746 | 65.0 °C |
| RTI Imp | 0.75mm | UL 746 | 105 °C |
| RTI Imp | 1.5mm | UL 746 | 105 °C |
| RTI Imp | 3.0mm | UL 746 | 105 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 224 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 91.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 70.0 °C |
| melting temperature | | ASTM D3418 | 243 °C |
| melting temperature | | ISO 3146 | 243 °C |
| Linear coefficient of thermal expansion | MD | ASTME831 | 4E-05 cm/cm/°C |
| RTI Str | 0.38mm | UL 746 | 65.0 °C |
| RTI Str | 0.75mm | UL 746 | 115 °C |
| RTI Str | 1.5mm | UL 746 | 120 °C |
| RTI Str | 3.0mm | UL 746 | 120 °C |