برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ThermalConductivityofMelt | | | 0.23 W/m/K |
| density | | ISO 1183 | 1.14 g/cm³ |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 17.0 cm³/10min |
| Shrinkage rate | MD | ISO 294-4 | 0.60 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.50 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 725 °C |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 700 °C |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 750 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 725 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 23 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/4A | 70 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 20 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 40 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -40°C | ISO 180/4A | 35 kJ/m² |
| Impact strength of cantilever beam gap | -20°C | ISO 180/4A | 60 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile strain | Yield | ISO 527-2 | 5.0 % |
| Nominal tensile fracture strain | | ISO 527-2 | >50 % |
| Flexural modulus | | ISO 178 | 2300 MPa |
| bending strength | | ISO 178 | 85.0 MPa |
| Tensile modulus | | ISO 527-2 | 2300 MPa |
| tensile strength | Yield | ISO 527-2 | 55.0 MPa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 35 kV/mm |
| relative permittivity | 1MHz | IEC 60250 | 2.90 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 110 °C |
| vicat | | ISO 306/B50 | 130 °C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.