PC XANTAR® C CM 506 U Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMitsubishi Chemical Corporation/XANTAR® C CM 506 U
Charpy Notched Impact Strength23°CISO 179/1eA40 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap23°CISO 180/4A70 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA20 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-40°CISO 180/4A35 kJ/m²
-20°CISO 180/4A60 kJ/m²
Electrical performanceTest ConditionTest MethodMitsubishi Chemical Corporation/XANTAR® C CM 506 U
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 2
dielectric strengthIEC 60243-135 kV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
relative permittivity1MHzIEC 602502.90
Surface ResistivityIEC 60093>1.0E+15 ohms
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 2
Mechanical propertiesTest ConditionTest MethodMitsubishi Chemical Corporation/XANTAR® C CM 506 U
Nominal tensile fracture strainISO 527-2>50 %
Tensile modulusISO 527-22300 MPa
Tensile strain屈服ISO 527-25.0 %
tensile strength 屈服ISO 527-255.0 MPa
Flexural modulusISO 1782300 MPa
bending strengthISO 17885.0 MPa
flammabilityTest ConditionTest MethodMitsubishi Chemical Corporation/XANTAR® C CM 506 U
UL flame retardant rating3.0mmIEC 60695-11-10,-20HB
Burning wire flammability index3.0mmIEC 60695-2-12700 °C
UL flame retardant rating1.5mmIEC 60695-11-10,-20HB
Burning wire flammability index1.5mmIEC 60695-2-12725 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13725 °C
1.5mmIEC 60695-2-13750 °C
Limiting Oxygen IndexISO 4589-223 %
physical property Test ConditionTest MethodMitsubishi Chemical Corporation/XANTAR® C CM 506 U
Shrinkage rateMDISO 294-40.60 %
Water absorption rate饱和,23°CISO 620.50 %
densityISO 11831.14 g/cm³
ThermalConductivityofMelt0.23 W/m/K
Melt volume flow rate260°C/5.0kgISO 113317.0 cm³/10min
Thermal performanceTest ConditionTest MethodMitsubishi Chemical Corporation/XANTAR® C CM 506 U
vicatISO 306/B50130 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A110 °C
Linear coefficient of thermal expansionMDISO 11359-27E-05 cm/cm/°C
TDISO 11359-27E-05 cm/cm/°C
ball-indentation hardness125°CIEC 60695-10-2Pass