XLPE Pexidan® X/T USA Saco Polymers

مقایسه

برگه داده فنی

AcidGasEmission-HBr	شرایط آزمون	روش آزمون	نتیجه آزمون
Acid gas release	HBr (溴化氢)	CSAC22.2No.0.3Method2	3.7 %

	شرایط آزمون	روش آزمون	نتیجه آزمون
brittle temperature		ASTM D746	<-75.0 °C
deformation		UL 1581	1.0 %
HotElongation	150°C	内部方法	40 %
insulation resistance	after12weeks:90°C	UL 1581	50000 Mohms/1000ft
Limiting Oxygen Index	4.00mm	ASTM D2863	24 %
CrushingTest		UL 1581	635029 g
density		ASTM D792	1.01 g/cm³
melt mass-flow rate	190°C/2.16kg	ASTM D1238	0.80 g/10min
Degree of crosslinking		ASTM D2765	67 %
tensile strength	Yield	UL 1581	12.4 MPa
	tensile strength	Break	UL 1581	13.8 MPa
		tensile strength	断裂2	UL 1581	13.4 MPa
			tensile strength	断裂3	UL 1581	12.8 MPa
			tensile strength	tensile strength	断裂4	UL 1581	12.6 MPa
elongation	Break	UL 1581	380 %
elongation	elongation	断裂2	UL 1581	350 %
dielectric constant	1MHz	ASTM D150	2.34
	dielectric constant	100MHz	ASTM D150	2.34
	dielectric constant	dielectric constant	90°C,60Hz	UL 1581	2.50
Dissipation Factor	1MHz	ASTM D150	1.2E-03
Dissipation Factor	Dissipation Factor	100MHz	ASTM D150	8E-04
dielectric strength	--	UL 1581	35000 V
dielectric strength	dielectric strength	afterglancingimpact	UL 1581	33000 V
insulation resistance	23°C	UL 1581	560000 Mohms/1000ft
insulation resistance	insulation resistance	90°C	UL 1581	21000 Mohms/1000ft
elongation	断裂3	UL 1581	330 %
WeatherometerAging	Elongationafterexposure	UL 1581	430 %
	WeatherometerAging	Originalelongation	UL 1581	440 %
		WeatherometerAging	Originaltensilestrength	UL 1581	18.3 MPa
		WeatherometerAging	WeatherometerAging	Tensilestrengthafterexposure	UL 1581	19.8 MPa