PAI 4310 USA Suwei

ویژگی‌ها:
Adding ingredients such as graphite powder fluorinated polymer a composite with high compressive strength versatility high performance low friction coefficient and wear resistance
کاربردها:
Bearings thrust washers wear pads slats piston rings seals blades and valve seats
مقایسه

برگه داده فنی

Basic Performance	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.47 g/cm3
Water absorption rate	24hr	ASTM D570	0.28 %

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	23℃	ASTM D1708	163 MPa
Elongation at Break	23℃	ASTM D1708	7 %
Tensile modulus	23℃	ASTM D790	6600 MPa
bending strength	23℃	ASTM D790	215 MPa
Bending modulus	23℃	ASTM D790	6900 MPa
compressive strength		ASTM D695	166 MPa
Compressive modulus		ASTM D695	5.3 MPa
shear strength	23℃	ASTM D732	112 MPa
Impact strength of cantilever beam gap	（Notched）3.2mm	ASTM D256	64 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Unnotched 3.2mm	ASTM D256	404 J/m
Poisson's ratio			0.39

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion		ASTM D696	25.2 ppm/°C
Hot deformation temperature	1.8MPa	ASTM D648	279 ℃
UL flame retardant rating		UL 94	V-0
Extreme Oxygen Index		ASTM D2863	44 %

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.