PA66 TAROMID A 280 X0 Taro Plast S.p.A.

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTMD792	1.22to1.24 g/cm³
Shrinkage rate	MD	ASTM D955	1.2to1.8 %
Shrinkage rate	Shrinkage rate	TD	ASTM D955	1.7to2.5 %
Water absorption rate	23°C,24hr	ASTMD570	1.0to1.5 %
	Water absorption rate	Saturation	ASTM D570	8.0 %
	Water absorption rate	Water absorption rate	饱和,23°C	ISO 62	8.0 %
GranuleHumidity		内部方法	<0.15 %

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	0.9mm	UL 94	V-0
Burning wire flammability index		IEC 60695-2-12	960 °C
Hot filament ignition temperature		IEC 60695-2-13	775 °C
Limiting Oxygen Index		ASTM D2863	30 %

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C,3.20mm	ASTMD256	40 J/m
Charpy Notched Impact Strength	23°C	ISO 179	3.6 kJ/m²
Impact strength of cantilever beam gap	-20°C,3.20mm	ASTMD256	22 J/m

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTMD638	3300 MPa
tensile strength	Yield	ASTMD638	84.0 MPa
tensile strength	tensile strength	Break	ASTMD638	80.0 MPa
elongation	Break	ASTMD638	5.0 %
Flexural modulus		ASTMD790	3100 MPa
bending strength	--3	ISO 178	130 MPa
	bending strength	--4	ISO 178	135 MPa
		bending strength	Yield	ASTM D790	135 MPa
		bending strength	bending strength	Break	ASTM D790	130 MPa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity		ASTM D257	1E+15 ohms·cm
dielectric strength	2.00mm	ASTM D149	22 kV/mm
Compared to the Leakage Tracking Index (CTI)	解决方案A	IEC 60112	PLC 2

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
melting temperature		ASTMD211	250to256 °C
Linear coefficient of thermal expansion	MD：-30到30°C	ASTM D696	1.2E-04 cm/cm/°C
Heat distortion temperature	0.45MPa,未退火，HDT	ASTMD648	220 °C
Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火，HDT	ASTMD648	98.0 °C
Continuous use temperature	--	UL 746B	65.0 °C
	Continuous use temperature	--6	IEC 60216	90.0 °C
		Continuous use temperature	--7	IEC 60216	100 °C
			Continuous use temperature	--8	IEC 60216	120 °C
			Continuous use temperature	Continuous use temperature	--9	IEC 60216	160 °C
vicat	--	ASTMD152510	250 °C
vicat	vicat	--	ASTMD152511	240 °C
ball-indentation hardness	165°C	VDE0470	通过