PA66 TAROMID A 280 X0 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 X0 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 3.6 kJ/m² |
| Impact strength of cantilever beam gap | -20°C,3.20mm | ASTMD256 | 22 J/m |
| 23°C,3.20mm | ASTMD256 | 40 J/m |
| Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 X0 |
|---|---|---|---|
| Flexural modulus | ASTMD790 | 3100 MPa | |
| elongation | 断裂 | ASTMD638 | 5.0 % |
| bending strength | 屈服 | ASTM D790 | 135 MPa |
| 断裂 | ASTM D790 | 130 MPa | |
| Tensile modulus | ASTMD638 | 3300 MPa | |
| tensile strength | 断裂 | ASTMD638 | 80.0 MPa |
| 屈服 | ASTMD638 | 84.0 MPa | |
| bending strength | --4 | ISO 178 | 135 MPa |
| --3 | ISO 178 | 130 MPa |
| Electrical performance | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 X0 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| dielectric strength | 2.00mm | ASTM D149 | 22 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 X0 |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 775 °C | |
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| UL flame retardant rating | 0.9mm | UL 94 | V-0 |
| Limiting Oxygen Index | ASTM D2863 | 30 % |
| physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 X0 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 1.2to1.8 % |
| Water absorption rate | 饱和 | ASTM D570 | 8.0 % |
| GranuleHumidity | 内部方法 | <0.15 % | |
| density | ASTMD792 | 1.22to1.24 g/cm³ | |
| Water absorption rate | 23°C,24hr | ASTMD570 | 1.0to1.5 % |
| 饱和,23°C | ISO 62 | 8.0 % | |
| Shrinkage rate | TD | ASTM D955 | 1.7to2.5 % |
| Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 X0 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTMD648 | 98.0 °C |
| 0.45MPa,未退火，HDT | ASTMD648 | 220 °C | |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 1.2E-04 cm/cm/°C |
| Continuous use temperature | -- | UL 746B | 65.0 °C |
| melting temperature | ASTMD211 | 250to256 °C | |
| Continuous use temperature | --7 | IEC 60216 | 100 °C |
| ball-indentation hardness | 165°C | VDE0470 | 通过 |
| Continuous use temperature | --6 | IEC 60216 | 90.0 °C |
| --9 | IEC 60216 | 160 °C | |
| vicat | -- | ASTMD152510 | 250 °C |
| Continuous use temperature | --8 | IEC 60216 | 120 °C |
| vicat | -- | ASTMD152511 | 240 °C |