برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 25.0 cm³/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.40to0.60 % |
| Shrinkage rate | MD | ISO 294-4 | 0.40to0.60 % |
| density | | ISO 1183 | 1.05 g/cm³ |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ball-indentation hardness | | ISO 2039-1 | 105 MPa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| burning rate | 2.00mm | ISO 3795 | 60 mm/min |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 700 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 2.5 % |
| Tensile strain | 断裂,23°C | ISO 527-2/50 | >15 % |
| Flexural modulus | 23°C | ISO 178 | 2400 MPa |
| bending strength | 23°C | ISO 178 | 72.0 MPa |
| Tensile modulus | 23°C | ISO 527-2/1 | 2400 MPa |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 47.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 17 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 80 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 17 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.10 |
| relative permittivity | 23°C,1MHz | IEC 60250 | 3.00 |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 5E-03 |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 8E-03 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 33 kV/mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 102 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 98.0 °C |
| vicat | | ISO 306/B50 | 101 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.