HDPE Safrene® H 4765 SAFRIPOL SOUTH AFRICA

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23°C,Compression Molded	ISO 179	13 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C,Compression Molded	ISO 179	9.0 kJ/m²

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Bending modulus		ISO 178	1450 MPa
Tensile strain	Break,Compression Molded	ISO 527-2/50	>600 %
tensile strength	Break,Compression Molded	ISO 527-2/50	34.0 MPa
tensile strength	tensile strength	Yield,Compression Molded	ISO 527-2/50	29.0 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Crystallization peak temperature	DSC	ISO 3146	130to133 °C
Vicat softening temperature	--	ISO 306/B50	78.0 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	128 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Environmental stress cracking resistance	50°C,10%Igepal,F50	ASTM D1693B	150 hr
melt mass-flow rate	190°C/5.0kg	ISO 1133	1.4 g/10min
melt mass-flow rate	melt mass-flow rate	190°C/2.16kg	ISO 1133	0.33 g/10min
density		ISO 1183	0.958 g/cm³

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	ShoreD,Compression Molded	ISO 868	64

Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون
Blow molding temperature	Zone3		180to190 °C
	Blow molding temperature	Zone2		180to200 °C
		Blow molding temperature	Zone1		170to190 °C
		Blow molding temperature	Blow molding temperature	FeedZone		160to180 °C
Blow molding melt temperature			190to200 °C
Blow molding mouth mold temperature			190to200 °C