Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HDPE Safrene® H 4765 SAFRIPOL SOUTH AFRICA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SAFRIPOL SOUTH AFRICA/Safrene® H 4765 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C,模压成型 | ISO 179 | 13 kJ/m² |
| -30°C,模压成型 | ISO 179 | 9.0 kJ/m² |
| hardness | Test Condition | Test Method | SAFRIPOL SOUTH AFRICA/Safrene® H 4765 |
|---|---|---|---|
| Shore hardness | 邵氏D,模压成型 | ISO 868 | 64 |
| Supplementary Information | Test Condition | Test Method | SAFRIPOL SOUTH AFRICA/Safrene® H 4765 |
|---|---|---|---|
| Blow molding melt temperature | 190to200 °C | ||
| Blow molding temperature | FeedZone | 160to180 °C | |
| Blow molding mouth mold temperature | 190to200 °C | ||
| Blow molding temperature | Zone3 | 180to190 °C | |
| Zone1 | 170to190 °C | ||
| Zone2 | 180to200 °C |
| Mechanical properties | Test Condition | Test Method | SAFRIPOL SOUTH AFRICA/Safrene® H 4765 |
|---|---|---|---|
| tensile strength | 屈服,模压成型 | ISO 527-2/50 | 29.0 MPa |
| Tensile strain | 断裂,模压成型 | ISO 527-2/50 | >600 % |
| tensile strength | 断裂,模压成型 | ISO 527-2/50 | 34.0 MPa |
| Flexural modulus | ISO 178 | 1450 MPa |
| physical property | Test Condition | Test Method | SAFRIPOL SOUTH AFRICA/Safrene® H 4765 |
|---|---|---|---|
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 1.4 g/10min |
| Environmental stress cracking resistance | 50°C,10%Igepal,F50 | ASTM D1693B | 150 hr |
| density | ISO 1183 | 0.958 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 0.33 g/10min |
| Thermal performance | Test Condition | Test Method | SAFRIPOL SOUTH AFRICA/Safrene® H 4765 |
|---|---|---|---|
| vicat | -- | ISO 306/A50 | 128 °C |
| -- | ISO 306/B50 | 78.0 °C | |
| Crystallization peak temperature | DSC | ISO 3146 | 130to133 °C |