PPC LEXAN™ HPH4404 resin SABIC
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D570 | 0.16 % |
| 饱和,23°C | ISO 62 | 0.16 % | |
| 平衡,23°C,50%RH | ISO 62 | 0.35 % | |
| melt mass-flow rate | 330°C/2.16kg | ASTM D1238 | 30 g/10min |
| Melt volume flow rate | 330°C/2.16kg | ISO 1133 | 29.0 cm³/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.60to0.80 % |
| density | ASTM D792 | 1.20 g/cm³ | |
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| density | ASTM D792 | 1.19 g/cm³ | |
| ISO 1183 | 1.20 g/cm³ | ||
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 6.0 g/10min |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 85 |
| R-Scale | ASTM D785 | 122 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| refractive index | ASTM D542 | 1.600 | |
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| transmissivity | 2540µm | ASTM D1003 | 85.0 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 57 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 600 J/m |
| -30°C | ISO 180/1A | 11 kJ/m² | |
| 23°C | ISO 180/1A | 53 kJ/m² | |
| 23°C | ASTM D4812 | NoBreak | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| 23°C | ISO 180/1U | NoBreak | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 120 J |
| 23°C | ASTM D3029 | 149 J | |
| Impact strength of cantilever beam gap | ASTM D1822 | 577 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 13 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2100 MPa | |
| ISO 527-2/1 | 2150 MPa | ||
| tensile strength | Yield | ASTM D638 | 65.0 MPa |
| Yield | ISO 527-2/50 | 65.0 MPa | |
| Break | ASTM D638 | 70.0 MPa | |
| Break | ISO 527-2/50 | 60.0 MPa | |
| elongation | Yield | ASTM D638 | 7.0 % |
| Tensile strain | Yield | ISO 527-2/50 | 7.0 % |
| elongation | Break | ASTM D638 | >110 % |
| Tensile strain | Break | ISO 527-2/50 | 85 % |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2200 MPa |
| ISO 178 | 2120 MPa | ||
| bending strength | ISO 178 | 66.0 MPa | |
| 屈服,50.0mm跨距 | ASTM D790 | 95.0 MPa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Dissipation Factor | 60Hz | ASTM D150 | 1.2E-03 |
| 100Hz | ASTM D150 | 0.024 | |
| Volume resistivity | ASTM D257 | >2.6E+17 ohms·cm | |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 20 kV/mm |
| dielectric constant | 50Hz | ASTM D150 | 3.15 |
| 60Hz | ASTM D150 | 3.15 | |
| 1MHz | ASTM D150 | 3.00 | |
| Dissipation Factor | 50Hz | ASTM D150 | 1.2E-03 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 125 °C |
| vicat | ASTM D152511 | 160 °C | |
| -- | ISO 306/B50 | 154 °C | |
| -- | ISO 306/B120 | 155 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 6E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 6E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 8E-05 cm/cm/°C | |
| TD：-40到40°C | ISO 11359-2 | 6E-05 cm/cm/°C | |
| specific heat | ASTMC351 | 1250 J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.21 W/m/K | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 142 °C |