PPC LEXAN™ HPH4404 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC/LEXAN™ HPH4404 resin |
---|---|---|---|
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
Impact strength of cantilever beam gap | 23°C | ASTM D256 | 600 J/m |
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 120 J |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
Impact strength of cantilever beam gap | ASTM D1822 | 577 kJ/m² | |
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 57 kJ/m² |
-30°C | ISO 179/1eA | 13 kJ/m² | |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 11 kJ/m² |
23°C | ASTM D4812 | NoBreak | |
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 53 kJ/m² |
Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
Dart impact | 23°C | ASTM D3029 | 149 J |
hardness | Test Condition | Test Method | SABIC/LEXAN™ HPH4404 resin |
---|---|---|---|
Rockwell hardness | M计秤 | ASTM D785 | 85 |
R计秤 | ASTM D785 | 122 |
Electrical performance | Test Condition | Test Method | SABIC/LEXAN™ HPH4404 resin |
---|---|---|---|
dielectric strength | 3.20mm,inAir | ASTM D149 | 20 kV/mm |
Dissipation Factor | 50Hz | ASTM D150 | 1.2E-03 |
60Hz | ASTM D150 | 1.2E-03 | |
dielectric constant | 60Hz | ASTM D150 | 3.15 |
Dissipation Factor | 100Hz | ASTM D150 | 0.024 |
Volume resistivity | ASTM D257 | >2.6E+17 ohms·cm | |
dielectric constant | 50Hz | ASTM D150 | 3.15 |
1MHz | ASTM D150 | 3.00 |
Mechanical properties | Test Condition | Test Method | SABIC/LEXAN™ HPH4404 resin |
---|---|---|---|
elongation | 屈服 | ASTM D638 | 7.0 % |
tensile strength | 屈服 | ASTM D638 | 65.0 MPa |
Flexural modulus | ISO 178 | 2120 MPa | |
Tensile strain | 屈服 | ISO 527-2/50 | 7.0 % |
tensile strength | 屈服 | ISO 527-2/50 | 65.0 MPa |
bending strength | ISO 178 | 66.0 MPa | |
elongation | 断裂 | ASTM D638 | >110 % |
bending strength | 屈服,50.0mm跨距 | ASTM D790 | 95.0 MPa |
Tensile modulus | ASTM D638 | 2100 MPa | |
tensile strength | 断裂 | ASTM D638 | 70.0 MPa |
Flexural modulus | 50.0mm跨距 | ASTM D790 | 2200 MPa |
Tensile strain | 断裂 | ISO 527-2/50 | 85 % |
Tensile modulus | ISO 527-2/1 | 2150 MPa | |
tensile strength | 断裂 | ISO 527-2/50 | 60.0 MPa |
optical performance | Test Condition | Test Method | SABIC/LEXAN™ HPH4404 resin |
---|---|---|---|
Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
refractive index | ASTM D542 | 1.600 | |
transmissivity | 2540µm | ASTM D1003 | 85.0 % |
physical property | Test Condition | Test Method | SABIC/LEXAN™ HPH4404 resin |
---|---|---|---|
Melt volume flow rate | 330°C/2.16kg | ISO 1133 | 29.0 cm³/10min |
Shrinkage rate | MD:3.20mm | 内部方法 | 0.60to0.80 % |
Water absorption rate | 24hr | ASTM D570 | 0.16 % |
平衡,23°C,50%RH | ISO 62 | 0.35 % | |
饱和,23°C | ISO 62 | 0.16 % | |
density | ASTM D792 | 1.19 g/cm³ | |
Specific volume | ASTM D792 | 0.830 cm³/g | |
melt mass-flow rate | 330°C/2.16kg | ASTM D1238 | 30 g/10min |
density | ISO 1183 | 1.20 g/cm³ | |
melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 6.0 g/10min |
Thermal performance | Test Condition | Test Method | SABIC/LEXAN™ HPH4404 resin |
---|---|---|---|
vicat | -- | ISO 306/B120 | 155 °C |
Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 8E-05 cm/cm/°C |
TD:-40到40°C | ISO 11359-2 | 6E-05 cm/cm/°C | |
thermal conductivity | ASTMC177 | 0.21 W/m/K | |
vicat | -- | ISO 306/B50 | 154 °C |
Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 6E-05 cm/cm/°C |
vicat | ASTM D152511 | 160 °C | |
Linear coefficient of thermal expansion | MD:-40到40°C | ISO 11359-2 | 6E-05 cm/cm/°C |
Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan,HDT | ISO 75-2/Af | 125 °C |
specific heat | ASTMC351 | 1250 J/kg/°C | |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 142 °C |