PPS+PPE NORYL GTX™ EXNX0080 resin SABIC

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Dart impact	23°C,TotalEnergy	ASTM D3763	3.60 J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	35 kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTM D256	37 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	34 J/m
		Impact strength of cantilever beam gap	-30°C8	ISO 180/1A	34 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C8	ISO 180/1A	34 kJ/m²

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Break3	ASTM D638	79.2 MPa
tensile strength	tensile strength	Break	ISO 527-2/5	89.0 MPa
elongation	Yield3	ASTM D638	0.64 %
	elongation	Yield	ISO 527-2/5	0.64 %
		elongation	Break3	ASTM D638	0.66 %
		elongation	elongation	Break	ISO 527-2/5	0.66 %
Bending modulus	50.0mmSpan4	ASTM D790	12700 MPa
Bending modulus	Bending modulus	--5	ISO 178	13600 MPa
bending strength	--5,6	ISO 178	0.980 MPa
bending strength	bending strength	Yield,50.0mmSpan4	ASTM D790	118 MPa
Tensile modulus	--2	ASTM D638	16300 MPa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	15000 MPa
tensile strength	Yield3	ASTM D638	79.2 MPa
tensile strength	tensile strength	Yield	ISO 527-2/5	89.0 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	234 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,100mmSpan9	ISO 75-2/Ae	229 °C
Vicat softening temperature	--	ASTMD152510	231 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	233 °C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	2.7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	4.9E-05 cm/cm/°C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTMD792	1.62 g/cm³
melt mass-flow rate	300°C/2.16kg	ASTM D1238	16 g/10min
Melt Volume Flow Rate (MVR)	300°C/2.16kg	ISO 1133	10.0 cm³/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.30to0.80 %
Water absorption rate	Saturation,23°C	ISO 62	0.020 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.0 %

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity		ASTM D257	2.5E+04 ohms·cm

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.