Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS+PPE NORYL GTX™ EXNX0080 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/NORYL GTX™ EXNX0080 resin |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 35 kJ/m² |
| Impact strength of cantilever beam gap | -30°C8 | ISO 180/1A | 34 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 3.60 J |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 37 J/m |
| 23°C | ASTM D256 | 34 J/m | |
| 23°C8 | ISO 180/1A | 34 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL GTX™ EXNX0080 resin |
|---|---|---|---|
| tensile strength | 屈服3 | ASTM D638 | 79.2 MPa |
| elongation | 断裂3 | ASTM D638 | 0.66 % |
| tensile strength | 屈服 | ISO 527-2/5 | 89.0 MPa |
| Flexural modulus | --5 | ISO 178 | 13600 MPa |
| Tensile modulus | -- | ISO 527-2/1 | 15000 MPa |
| bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 118 MPa |
| elongation | 屈服 | ISO 527-2/5 | 0.64 % |
| Flexural modulus | 50.0mm跨距4 | ASTM D790 | 12700 MPa |
| tensile strength | 断裂 | ISO 527-2/5 | 89.0 MPa |
| bending strength | --5,6 | ISO 178 | 0.980 MPa |
| elongation | 屈服3 | ASTM D638 | 0.64 % |
| tensile strength | 断裂3 | ASTM D638 | 79.2 MPa |
| elongation | 断裂 | ISO 527-2/5 | 0.66 % |
| Tensile modulus | --2 | ASTM D638 | 16300 MPa |
| Electrical performance | Test Condition | Test Method | SABIC/NORYL GTX™ EXNX0080 resin |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 2.5E+04 ohms·cm |
| physical property | Test Condition | Test Method | SABIC/NORYL GTX™ EXNX0080 resin |
|---|---|---|---|
| melt mass-flow rate | 300°C/2.16kg | ASTM D1238 | 16 g/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.30to0.80 % |
| density | ASTMD792 | 1.62 g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.0 % |
| 饱和,23°C | ISO 62 | 0.020 % | |
| Melt volume flow rate | 300°C/2.16kg | ISO 1133 | 10.0 cm³/10min |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL GTX™ EXNX0080 resin |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 4.9E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 233 °C |
| -- | ASTMD152510 | 231 °C | |
| Heat distortion temperature | 1.8MPa,未退火,100mm跨距9，HDT | ISO 75-2/Ae | 229 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 234 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 2.7E-05 cm/cm/°C |