برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| MeltViscosity | 400°C,1000sec^-1 | ASTM D3835 | 300 Pa·s |
| density | | | 1.30 g/cm³ |
| spiral flow length | | ASTM D3123 | 33.7 cm |
| Shrinkage rate | MD3 | | 1.1 % |
| Shrinkage rate | TD3 | | 1.3 % |
| Water absorption rate | Equilibrium | ASTM D570 | 0.060 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 98 |
| Shore hardness | 邵氏D | ASTM D2240 | 87 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation | 断裂,23°C | ASTM D638 | 20to25 % |
| Flexural modulus | 23°C | ASTM D790 | 4100 MPa |
| bending strength | 23°C | ASTM D790 | 185 MPa |
| compressive strength | | ASTM D695 | 135 MPa |
| Tensile modulus | 23°C | ASTM D638 | 4200 MPa |
| tensile strength | 屈服,23°C | ASTM D638 | 110 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 60 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | NoBreak |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Glass Transition Temperature | | ASTM D3418 | 152 °C |
| melting temperature | | ASTM D3418 | 372 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 175 °C |
| Continuous use temperature | | UL 746B | 280 °C |