AES+PC+AS(SAN) LNP™ LUBRICOMP™ Lexan_WR6300 compound SABIC

مقایسه

برگه داده فنی

	شرایط آزمون	روش آزمون	نتیجه آزمون
vicat		ASTM D15255	137 °C
Melt volume flow rate	300°C/2.16kg	ISO 1133	38.0 cm³/10min
Shrinkage rate	MD：3.20mm	内部方法	0.50to0.70 %
tensile strength	Yield	ASTM D638	60.7 MPa
tensile strength	tensile strength	Break	ASTM D638	61.4 MPa
elongation	Break	ASTM D638	160 %
density		ASTM D792	1.17 g/cm³
Melt volume flow rate	300°C/2.16kg	ISO 1133	38.0 cm³/10min
Shrinkage rate	MD：3.20mm	内部方法	0.50to0.70 %
tensile strength	Yield	ASTM D638	60.7 MPa
tensile strength	tensile strength	Break	ASTM D638	61.4 MPa
elongation	Break	ASTM D638	160 %
Flexural modulus	50.0mm跨距	ASTM D790	2490 MPa
bending strength	屈服,50.0mm跨距	ASTM D790	96.5 MPa
Impact strength of cantilever beam gap	-30°C	ASTM D256	170 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	680 J/m
Suspended wall beam without notch impact strength	23°C	ASTM D4812	2500 J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	60.2 J
Heat distortion temperature	0.45MPa,未退火,6.40mm，HDT	ASTM D648	134 °C
	Heat distortion temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	117 °C
	Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火,6.40mm，HDT	ASTM D648	121 °C
Impact strength of cantilever beam gap	23°C	ASTM D256	680 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	2500 J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	60.2 J
Heat distortion temperature	0.45MPa,未退火,6.40mm，HDT	ASTM D648	134 °C
	Heat distortion temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	117 °C
	Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火,6.40mm，HDT	ASTM D648	121 °C
vicat		ASTM D15254	137 °C
RTI Elec		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI		UL 746	80.0 °C
Linear coefficient of thermal expansion	MD：-40到40°C	ASTME831	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40到40°C	ASTME831	1.2E-04 cm/cm/°C
RTI Elec		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI Str		UL 746	80.0 °C
UL flame retardant rating	1.5mm	UL 94	HB
Flexural modulus	50.0mm跨距	ASTM D790	2490 MPa
bending strength	屈服,50.0mm跨距	ASTM D790	96.5 MPa
Impact strength of cantilever beam gap	-30°C	ASTM D256	170 J/m
UL flame retardant rating	1.50mm	UL 94	HB
density		ASTM D792	1.17 g/cm³
Linear coefficient of thermal expansion	MD:-40到40°C	ASTME831	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40到40°C	ASTME831	1.2E-04 cm/cm/°C