AES+PC+AS(SAN) LNP™ LUBRICOMP™ Lexan_WR6300 compound SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | SABIC/LNP™ LUBRICOMP™ Lexan_WR6300 compound | |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 2500 J/m |
| tensile strength | 屈服 | ASTM D638 | 60.7 MPa |
| elongation | 断裂 | ASTM D638 | 160 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 96.5 MPa |
| RTI Elec | UL 746 | 80.0 °C | |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 170 J/m |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 2500 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 60.2 J |
| UL flame retardant rating | 1.50mm | UL 94 | HB |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 117 °C |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 1.2E-04 cm/cm/°C |
| density | ASTM D792 | 1.17 g/cm³ | |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 121 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| Melt volume flow rate | 300°C/2.16kg | ISO 1133 | 38.0 cm³/10min |
| vicat | ASTM D15255 | 137 °C | |
| RTI Str | UL 746 | 80.0 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI | UL 746 | 80.0 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 680 J/m |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1.2E-04 cm/cm/°C |
| tensile strength | 断裂 | ASTM D638 | 61.4 MPa |
| vicat | ASTM D15254 | 137 °C | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2490 MPa |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 134 °C |