SBC K-Resin® SBC KR52 USA Chevron Phillips
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| elongation | Break | ASTM D882 | 260 % |
| Water Vapor Transmission Rate | ASTMF1249 | 2.0 g·mm/m²/atm/24hr | |
| Dart impact | ASTM D3763 | 3.00 J | |
| vicat | ISO 306 | 60.0 °C | |
| gloss | ASTM D523 | 145 | |
| Haze ratio | ASTM D1003 | 4.0 % | |
| tensile strength | Break | ASTM D882 | 90.0 MPa |
| density | ASTM D792 | 1.01 g/cm³ | |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 9.0 g/10min |
| coefficient of friction | Itself - Dynamic | ASTM D1894 | 0.25 |
| Secant modulus | ASTM D882 | 1100 MPa | |
| ASTM D882 | 1600 MPa | ||
| tensile strength | Yield | ASTM D882 | 30.0 MPa |
| Yield | ASTM D882 | 45.0 MPa | |
| Break | ASTM D882 | 20.0 MPa | |
| Tensile strain | Break | ASTM D882 | 80 % |
| Elmendorf tear strength | MD | ASTM D1922 | 95 g |
| TD | ASTM D1922 | 75 g | |
| OTr | ASTM D3985 | 85 cm³·mm/m²/atm/24hr |