PPO(PPE)+PS+PP NORYL™ WCV072 resin

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.03 g/cm³
density	density		ISO 1183	1.03 g/cm³
melt mass-flow rate	280°C/5.0kg	ASTM D1238	14 g/10min
Melt volume flow rate	280°C/5.0kg	ISO 1133	13.4 cm³/10min
Water absorption rate	饱和,23°C	ISO 62	0.12 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.050 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Break	ASTM D638	41.5 MPa
tensile strength	tensile strength	Break	ISO 527-2/50	42.1 MPa
elongation	Yield	ASTM D638	15 %
Tensile strain	Yield	ISO 527-2/50	11 %
elongation	Break	ASTM D638	83 %
Tensile strain	Break	ISO 527-2/50	46 %
Flexural modulus	50.0mm跨距	ASTM D790	1560 MPa
Flexural modulus	Flexural modulus		ISO 178	1750 MPa
bending strength		ISO 178	59.3 MPa
bending strength	bending strength	屈服,50.0mm跨距	ASTM D790	53.2 MPa
Tensile modulus		ASTM D638	1710 MPa
Tensile modulus	Tensile modulus		ISO 527-2/1	1760 MPa
tensile strength	Yield	ASTM D638	43.8 MPa
tensile strength	tensile strength	Yield	ISO 527-2/50	44.6 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23°C	ISO 179/1eA	34 kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTM D256	67 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	310 J/m
		Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.9 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	37 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	45.9 J

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
vicat	--	ISO 306/B120	117 °C
Linear coefficient of thermal expansion	MD：-40到40°C	ASTME831	8.5E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40到40°C	ISO 11359-2	8.4E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40到40°C	ASTME831	1.1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40到40°C	ISO 11359-2	1.1E-04 cm/cm/°C
Heat distortion temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	92.0 °C
Heat distortion temperature	Heat distortion temperature	1.8MPa,Unannealed,64.0mmSpan，HDT	ISO 75-2/Af	98.0 °C
vicat		ASTM D152510	114 °C
vicat	vicat	--	ISO 306/B50	114 °C