Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO(PPE)+PS+PP NORYL™ WCV072 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/NORYL™ WCV072 resin |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 34 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 67 J/m |
| 23°C | ASTM D256 | 310 J/m | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 45.9 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.9 kJ/m² |
| 23°C | ISO 180/1A | 37 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL™ WCV072 resin |
|---|---|---|---|
| elongation | 屈服 | ASTM D638 | 15 % |
| tensile strength | 屈服 | ASTM D638 | 43.8 MPa |
| Flexural modulus | ISO 178 | 1750 MPa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 11 % |
| bending strength | ISO 178 | 59.3 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 44.6 MPa |
| elongation | 断裂 | ASTM D638 | 83 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 53.2 MPa |
| tensile strength | 断裂 | ASTM D638 | 41.5 MPa |
| Tensile modulus | ASTM D638 | 1710 MPa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 1560 MPa |
| Tensile strain | 断裂 | ISO 527-2/50 | 46 % |
| Tensile modulus | ISO 527-2/1 | 1760 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 42.1 MPa |
| physical property | Test Condition | Test Method | SABIC/NORYL™ WCV072 resin |
|---|---|---|---|
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 13.4 cm³/10min |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 14 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.050 % |
| 饱和,23°C | ISO 62 | 0.12 % | |
| density | ASTM D792 | 1.03 g/cm³ | |
| ISO 1183 | 1.03 g/cm³ |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL™ WCV072 resin |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 117 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 8.5E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 114 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 8.4E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 98.0 °C |
| vicat | ASTM D152510 | 114 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 92.0 °C |
Contact Us
Get App
Top