برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.18 g/cm³ |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 10 g/10min |
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 15 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.50to0.70 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.50mm | UL 94 | V-2 |
| UL flame retardant rating | 1.0mm | UL 94 | V-0 |
| UL flame retardant rating | 2.0mm | UL 94 | 5VB5VB |
| Burning wire flammability index | 0.50mm | IEC 60695-2-12 | 960 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | Yield | ASTM D638 | 60.0 MPa |
| elongation | Break | ASTM D638 | 60 % |
| Flexural modulus | | ASTM D790 | 2500 MPa |
| bending strength | | ASTM D790 | 88.3 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 720 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | 11 ohms·cm |
| dielectric strength | | ASTM D149 | 20 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 80.0 °C |
| vicat | | ASTM D15253 | 102 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.