| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | -- | ASTM D792 | 1.20 g/cm³ |
| density | 23°C | ISO 1183 | 1.19 g/cm³ |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.20to0.60 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R级,23°C | ASTM D785 | 103 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transmissivity | 常规 | ASTM D1003 | 89.0 % |
| transmissivity | 总计 | ASTM D1003 | 91.0 % |
| Haze ratio | | ASTM D1003 | 0.30 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Suspended wall beam without notch impact strength | -40°C | ASTM D4812 | 无断裂 |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 无断裂 |
| Dart impact | -40°C,EnergyatPeakLoad | ASTM D3763 | 48.0 J |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 42.0 J |
| Dart impact | -40°C,能量到力量峰值 | ISO 6603-2 | 52.6 J |
| Dart impact | 23°C,能量到力量峰值 | ISO 6603-2 | 58.7 J |
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 40 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 80 J/m |
| Impact strength of cantilever beam gap | -40°C | ISO 180 | 4.8 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 7.8 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ISO 527-2 | 1800 MPa |
| tensile strength | 屈服,23°C | ASTMD638 | 47.0 MPa |
| tensile strength | 断裂,23°C | ASTM D638 | 51.0 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 46.0 MPa |
| elongation | 屈服,23°C | ASTM D638 | 5.0 % |
| elongation | 屈服,23°C | ISO 527-2 | 4.0 % |
| elongation | 断裂,23°C | ASTM D638 | 300 % |
| elongation | 断裂,23°C | ISO 527-2 | 200 % |
| Flexural modulus | 23°C | ASTM D790 | 2000 MPa |
| Flexural modulus | 23°C | ISO 178 | 1850 MPa |
| bending strength | 23°C | ISO 178 | 65.0 MPa |
| bending strength | 屈服,23°C | ASTM D790 | 69.0 MPa |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 75.0 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 72.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 65.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 66.0 °C |