| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | TD:4.00mm | 内部方法 | 0.40-0.60 % |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.35-0.55 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.16 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.40mm | UL 94 | HB |
| UL flame retardant rating | 1.7mm | UL 94 | V-2 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2/1 | 3000 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 65.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/5 | 5.0 % |
| Flexural modulus | | ISO 178 | 3100 Mpa |
| bending strength | | ISO 178 | 110 Mpa |
| elongation at break | | ASTM D638/ISO 527 | 5.0 % |
| Tensile modulus | | ASTM D638/ISO 527 | 3000 kg/cm²(MPa)[Lb/in²] |
| Flexural modulus | | ASTM D790/ISO 178 | 3100 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 110 kg/cm²(MPa)[Lb/in²] |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 55 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 35 KV/mm |
| relative permittivity | 100Hz | IEC 60250 | 3.20 |
| relative permittivity | 1MHz | IEC 60250 | 3.20 |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| Dissipation Factor | 1MHz | IEC 60250 | 9E-03 |
| Physical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792/ISO 1183 | 1270 |
| Shrinkage rate | | ASTM D955 | 0.35-0.55 % |
| Water absorption rate | | ASTM D570/ISO 62 | 0.16 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 130 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 123 °C |
| vicat | | ISO 306/B50 | 134 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 6E-05 cm/cm/°C |
| RTI Elec | 1.7mm | UL 746 | 130 °C |
| RTI Imp | 1.7mm | UL 746 | 120 °C |
| RTI Str | 1.7mm | UL 746 | 130 °C |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 123 ℃（℉） |
| vicat | | ASTM D1525/ISO R306 | 134 ℃（℉） |
| Linear coefficient of thermal expansion | | ASTM D696/ISO 11359 | 0.5 mm/mm.℃ |