PC+TPU II 90A DSM Additive Manufacturing
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| average molecular weight | 内部方法 | 262000 Mw | |
| melt mass-flow rate | ASTM D1238 | 18 g/10min | |
| Shrinkage rate | MD | ASTM D955 | 0.83to2.7 % |
| Water absorption rate | Saturation | ASTM D750 | 0.72 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shore hardness | Shore A | ASTM D2240 | 92 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | 100%应变 | ASTM D1708 | 13.2 MPa |
| Flexural modulus | ASTM D790 | 45.1 MPa | |
| bending strength | 5.0%应变 | ASTM D790 | 2.16 MPa |
| coefficient of friction | Itself - Dynamic | ASTM D1894 | 0.43 |
| tensile strength | Break | ASTM D1708 | 59.4 MPa |
| 50%应变 | ASTM D1708 | 9.36 MPa | |
| 300%应变 | ASTM D1708 | 44.9 MPa | |
| elongation | Break | ASTM D1708 | 390 % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| dielectric strength | ASTM D149 | 17 kV/mm | |
| dielectric constant | 60Hz | ASTM D150 | 3.97 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Glass Transition Temperature | ASTME1356 | -2.00 °C | |
| vicat | ASTM D1525 | 94.7 °C | |
| melting temperature | ASTME1356 | 177 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.