PA6 Tarnamid® T-27 GF 15 MW 25 Grupa Azoty ATT Polymers GmbH
0
- ویژگیها:Fillerglass fiber reinforced material15%filler by weightmineral filler25%filler by weight
- کاربردها:Applications in the fields of electrical applianceshousehold goodsautomobileselectrical and electronic applications
برگه داده فنی
physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
density | ISO 1183 | 1.40 g/cm³ | |
Shrinkage rate | MD | ISO 294-4 | 0.001 % |
TD | ISO 294-4 | 0.01 % | |
Water absorption rate | (23°C,24hr) | ISO 62 | 1.1 % |
melt mass-flow rate | 275℃/5Kg | ISO 1133 | 60 cm³/10min |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
elongation at break | 23°C | ISO 527-2 | 3 % |
Tensile modulus | 23°C | ISO 527-2 | 10700 MPa |
bending strength | 3.5%弯曲,23°C | ISO 178 | <=165 MPa |
Flexural modulus | 23°C | ISO 178 | 9400 MPa |
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.5 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 42 kJ/m² |
tensile strength | 23°C | ISO 527-2 | 110 MPa |
Flame retardant performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
UL flame retardant rating | UL -94 | HB 1.6mm |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
Heat distortion temperature | 1.80MPa退火,HDT | ISO 75-2/A | 195 °C |
vicat | 干,5.1kg | ISO 306/B50 | 210 °C |
Melting Temperature | ISO 11357-3 | 221 °C |