| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| viscosity number | | ISO 307 | 110 cm³/g |
| Shrinkage rate | free,longitudinal | | 0.32 % |
| Shrinkage rate | free,transverse | | 0.99 % |
| density | | ISO 1183 | 1.33 g/cm³ |
| Apparent density | | | 0.70to0.80 g/cm³ |
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 23.0 cm³/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.83 % |
| Shrinkage rate | MD | ISO 294-4 | 0.54 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.40 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flammability level | 0.800mm | IEC 60695-11-10,-20 | HB |
| Flammability level | 1.60mm | IEC 60695-11-10,-20 | HB |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Automotive Materials | >1.00mm | FMVSS302 | Passed |
| ISOType | | ISO 7792 | PBT-ASA.MCGHLPR.11-060.GF14 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2 | 5500 MPa |
| tensile strength | Break | ISO 527-2 | 95.0 MPa |
| Tensile strain | Break | ISO 527-2 | 3.2 % |
| bending strength | | ISO 178 | 140 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 43 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 52 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| relative permittivity | 1MHz | IEC 60250 | 3.40 |
| Dissipation Factor | 100Hz | IEC 60250 | 3.9E-03 |
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| Dissipation Factor | 1MHz | IEC 60250 | 0.021 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| specific heat | | | 1070 J/kg/°C |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 5.2E-05 cm/cm/°C |
| melting temperature | | ISO 11357-3 | 223 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.