PBT+ASA Ultradur® S 4090 GX BASF GERMANY
--
Connectors, casings, engineering accessories
Filler, glass fiber reinforced material, 14%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/Ultradur® S 4090 GX |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 52 kJ/m² |
| -30°C | ISO 179/1eU | 43 kJ/m² |
| Supplementary Information | Test Condition | Test Method | BASF GERMANY/Ultradur® S 4090 GX |
|---|---|---|---|
| Automotive Materials | >1.00mm | FMVSS302 | Passed |
| ISOType | ISO 7792 | PBT-ASA.MCGHLPR.11-060.GF14 |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/Ultradur® S 4090 GX |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| Dissipation Factor | 100Hz | IEC 60250 | 3.9E-03 |
| relative permittivity | 1MHz | IEC 60250 | 3.40 |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.021 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/Ultradur® S 4090 GX |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 5500 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 95.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 3.2 % |
| bending strength | ISO 178 | 140 MPa |
| flammability | Test Condition | Test Method | BASF GERMANY/Ultradur® S 4090 GX |
|---|---|---|---|
| Flammability level | 0.800mm | IEC 60695-11-10,-20 | HB |
| 1.60mm | IEC 60695-11-10,-20 | HB |
| physical property | Test Condition | Test Method | BASF GERMANY/Ultradur® S 4090 GX |
|---|---|---|---|
| Apparent density | 0.70to0.80 g/cm³ | ||
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 23.0 cm³/10min |
| Shrinkage rate | free,longitudinal | 0.32 % | |
| TD | ISO 294-4 | 0.83 % | |
| viscosity number | ISO 307 | 110 cm³/g | |
| Shrinkage rate | MD | ISO 294-4 | 0.54 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.40 % | |
| density | ISO 1183 | 1.33 g/cm³ | |
| Shrinkage rate | free,transverse | 0.99 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/Ultradur® S 4090 GX |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 223 °C | |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 5.2E-05 cm/cm/°C |
| specific heat | 1070 J/kg/°C |