| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale, 23°C | ASTM D785 | 109 |
| thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat Deflection Temperature | 0.45 MPa, 未Annealed | ASTM D648 | 101 °C |
| Heat Deflection Temperature | 1.8 MPa, 未Annealed | ASTM D648 | 88.0 °C |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transmissivity | Total | ASTM D1003 | 91.0 % |
| haze | -- | ASTM D1003 | < 1.0 % |
| haze | --3 | Internal Method | < 6.0 % |
| shrinkage rate | Boiling, 1 hr | Internal Method | 1.9 % |
| shrinkage rate | Boiling, 2 hr | Internal Method | 2.3 % |
| shrinkage rate | Dishwasher | Internal Method | 0.0 % |
| Physical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| shrinkage rate | Injection，Flow | ASTM D955 | 0.50 - 0.70 % |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 88 °C |
| drying time | | | 4.0 to 6.0 hr |
| Processing (melt) temperature | | | 260 to 282 °C |
| mold temperature | | | 38 to 66 °C |
| mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile modulus | 23°C | ASTM D638 | 1520 Mpa |
| tensile modulus | 23°C | ISO 527-2 | 1540 Mpa |
| tensile strength | Yield, 23°C | ASTM D638 | 45.0 Mpa |
| tensile strength | Yield, 23°C | ISO 527-2 | 44.0 Mpa |
| tensile strength | Break, 23°C | ASTM D638 | 56.0 Mpa |
| tensile strength | Break, 23°C | ISO 527-2 | 55.0 Mpa |
| elongation | Yield, 23°C | ASTM D638 | 6.0 % |
| elongation | Break, 23°C | ASTM D638 | 180 % |
| elongation | Break, 23°C | ISO 527-2 | 150 % |
| bending strength | Yield, 23°C | ASTM D790 | 72.0 Mpa |
| impact performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Suspended wall beam without notch impact strength | -40°C | ASTM D4812 | 无断裂 |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 无断裂 |
| Dart impact | -40°C, Energy at Max Load | ASTM D3763 | 66.0 J |
| Dart impact | 23°C, Energy at Max Load | ASTM D3763 | 57.0 J |
| Dart impact | | Internal Method | No Crazes/No Impact Failures |