| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.08 g/cm³ |
| density | | ISO 1183 | 1.08 g/cm³ |
| Shrinkage rate | MD | ASTM D955 | 1.5to2.0 % |
| Shrinkage rate | | ISO 2577 | 1.5to2.0 % |
| Water absorption rate | Saturation | ASTM D570 | 5.6 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 5.6 % |
| Water absorption rate | 平衡,23°C,50%RH | ASTM D570 | 2.0 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.0 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ISO 2039-2 | 118 |
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | Yield | ASTM D638 | 45.0 MPa |
| tensile strength | Yield | ISO 527-2 | 45.0 MPa |
| elongation | Break | ASTM D638 | 100 % |
| Tensile strain | Break | ISO 527-2 | 100 % |
| Flexural modulus | | ASTM D790 | 1450 MPa |
| Flexural modulus | | ISO 178 | 1450 MPa |
| bending strength | | ASTM D790 | 65.0 MPa |
| Tensile modulus | | ASTM D638 | 1500 MPa |
| Tensile modulus | | ISO 527-2 | 1500 MPa |
| bending strength | | ISO 178 | 65.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179 | 45 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 100 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | NoBreak |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 520 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 1100 J/m |
| Impact strength of cantilever beam gap | -30°C | ISO 180 | 48 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 85 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| dielectric strength | | IEC 60243-1 | 90 kV/mm |
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| dielectric constant | 1MHz | IEC 60250 | 3.10 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 160 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 80.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 80.0 °C |
| maximum service temperature | | | 180 °C |
| melting temperature | | ASTM D3417 | 256 °C |
| melting temperature | | ISO 11357-3 | 256 °C |
| Continuous use temperature | | | 70 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 160 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.