PA66 PLUSTEK PA860 POLYRAM ISRAEL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PA860 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 100 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 520 J/m |
| 23°C | ASTM D256 | 1100 J/m | |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 45 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 85 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180 | 48 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | NoBreak |
| hardness | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PA860 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 118 |
| R级 | ASTM D785 | 118 |
| Electrical performance | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PA860 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 90 kV/mm | |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric constant | 1MHz | IEC 60250 | 3.10 |
| Surface Resistivity | IEC 60093 | 1E+13 ohms |
| Mechanical properties | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PA860 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 100 % |
| Tensile strain | 断裂 | ISO 527-2 | 100 % |
| Flexural modulus | ASTM D790 | 1450 MPa | |
| Tensile modulus | ASTM D638 | 1500 MPa | |
| ISO 527-2 | 1500 MPa | ||
| tensile strength | 屈服 | ASTM D638 | 45.0 MPa |
| 屈服 | ISO 527-2 | 45.0 MPa | |
| Flexural modulus | ISO 178 | 1450 MPa | |
| bending strength | ASTM D790 | 65.0 MPa | |
| ISO 178 | 65.0 MPa |
| flammability | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PA860 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| physical property | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PA860 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 1.5to2.0 % | |
| MD | ASTM D955 | 1.5to2.0 % | |
| Water absorption rate | 饱和 | ASTM D570 | 5.6 % |
| 平衡,23°C,50%RH | ASTM D570 | 2.0 % | |
| 平衡,23°C,50%RH | ISO 62 | 2.0 % | |
| 饱和,23°C | ISO 62 | 5.6 % | |
| density | ASTM D792 | 1.08 g/cm³ | |
| ISO 1183 | 1.08 g/cm³ |
| Thermal performance | Test Condition | Test Method | POLYRAM ISRAEL/PLUSTEK PA860 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 80.0 °C |
| melting temperature | ISO 11357-3 | 256 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 160 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 160 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 80.0 °C | |
| melting temperature | ASTM D3417 | 256 °C | |
| Continuous use temperature | 70 °C | ||
| maximum service temperature | 180 °C |