SBC Styrolux® 684D INEOS Barex

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	200°C/5.0kg	ASTM D1238	11 g/10min
Water absorption rate	饱和,23°C	ASTM D570	0.070 %
Water absorption rate	Water absorption rate	饱和,23°C	ISO 62	0.070 %
Melt volume flow rate	200°C/5.0kg	ISO 1133	11.0 cm³/10min
Shrinkage rate	MD	ASTM D955	0.65 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.30to1.0 %
density		ASTM D792	1.01 g/cm³
density	density		ISO 1183	1.01 g/cm³

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	邵氏D	ASTM D2240	68
Shore hardness	Shore hardness	邵氏D	ISO 868	68

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
refractive index		ASTM D542	1.575
refractive index	refractive index		ISO 489	1.575
transmissivity	550nm	ASTM D1003	90.0 %
Haze ratio		ASTM D1003	1.5 %

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
Impact strength of cantilever beam gap	23°C	ASTM D256	43 J/m
	Impact strength of cantilever beam gap	-30°C	ISO 180/A	3.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/A	4.0 kJ/m²
Dart impact	Peakforce	ASTM D3763	11.0 J
Dart impact	Dart impact	Totalenergy	ASTM D3763	22.1 J
Charpy Notched Impact Strength	23°C	ISO 179	4.0 kJ/m²

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
elongation	断裂,23°C	ASTM D638	250 %
Nominal tensile fracture strain	23°C	ISO 527-2	160 %
Tensile creep modulus	1hr	ISO 899-1	1300 MPa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	790 MPa
Tensile modulus		ASTM D638	1310 MPa
Tensile modulus	Tensile modulus		ISO 527-2	1500 MPa
tensile strength	屈服,23°C	ASTM D638	26.0 MPa
tensile strength	tensile strength	屈服,23°C	ISO 527-2	26.0 MPa
Tensile strain	屈服,23°C	ISO 527-2	2.3 %
Flexural modulus		ASTM D790	1170 MPa
Flexural modulus	Flexural modulus		ISO 178	1700 MPa
bending strength		ASTM D790	31.0 MPa
bending strength	bending strength		ISO 178	40.0 MPa

film	شرایط آزمون	روش آزمون	نتیجه آزمون
elongation	Break	ASTM D882	260 %
Tensile strain	Break	ASTM D882	100 %
elongation	Break	ISO 527-3	160 %
Elmendorf tear strength	MD	ASTM D1922	250 g
Elmendorf tear strength	Elmendorf tear strength	TD	ASTM D1922	240 g
OTr	23°C,0%RH	ASTM D3985	120000 cm³/m²/24hr
Water Vapor Transmission Rate	23°C	ASTMF1249	700 g/m²/24hr
Tensile modulus	MD	ASTM D882	1320 MPa
Tensile modulus	Tensile modulus	TD	ASTM D882	1180 MPa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
dielectric constant	100Hz	IEC 60250	2.50
Dissipation Factor	100Hz	IEC 60250	3E-04
Dissipation Factor	Dissipation Factor	1MHz	IEC 60250	8E-04
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 0
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
dielectric constant	1.00mm,1MHz	ASTM D150	2.50
Surface Resistivity		ASTM D257	>1.0E+14 ohms
Surface Resistivity	Surface Resistivity		IEC 60093	1E+15 ohms
Volume resistivity		ASTM D257	>1.0E+15 ohms·cm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火，HDT	ASTM D648	76.7 °C
	Heat distortion temperature	0.45MPa,Annealed，HDT	ISO 75-2/B	75.0 °C
		Heat distortion temperature	1.8MPa,未退火，HDT	ASTM D648	70.0 °C
		Heat distortion temperature	Heat distortion temperature	1.8MPa,Annealed，HDT	ISO 75-2/A	65.0 °C
vicat		ASTM D15254	85.6 °C
	vicat	--	ISO 306/A50	83.0 °C
	vicat	vicat	--	ISO 306/B50	59.0 °C
Linear coefficient of thermal expansion	MD	ASTM D696	1.3E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	6.0E-5to9.0E-5 cm/cm/°C