برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | -- | ASTM D792 | 1.05 g/cm³ |
| density | 23°C | ISO 1183 | 1.05 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 7.0 g/10min |
| melt mass-flow rate | 230°C/3.8kg | ISO 1133 | 7.0 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.50 % |
| Shrinkage rate | TD | ASTM D955 | 0.50 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 85 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| burning rate | | SAEJ369 | 45 mm/min |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/eA | 15 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 170 J/m |
| Dart impact | -29°C | ASTM D5420 | 4.00 J |
| Dart impact | 23°C | ASTM D5420 | 15.0 J |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2/1 | 2000 MPa |
| tensile strength | 屈服2 | ASTM D638 | 36.0 MPa |
| tensile strength | Yield | ISO 527-2/50 | 35.0 MPa |
| Flexural modulus | --3 | ASTM D790 | 2100 MPa |
| Flexural modulus | --4 | ISO 178 | 2200 MPa |
| bending strength | --3 | ASTM D790 | 62.0 MPa |
| bending strength | --4 | ISO 178 | 58.0 MPa |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 80.0 °C |
| vicat | | ISO 306/B50 | 86.0 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 90.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.