ABS M/SHI Schulman Plastics

ویژگی‌ها:
Impact modification
مقایسه

برگه داده فنی

Basic Performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Melt Volume Flow Rate (MVR)	220℃,10kg	ISO 1133	10.0 cm
density		ISO 1183	1.05

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of simply supported beam without notch	23℃	ISO 179/1eU	No Break KJ/m
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30℃	ISO 179/1eU	93.0 KJ/m
Charpy Notched Impact Strength	23℃	ISO 179/1eA	27.0 KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30℃	ISO 179/1eA	11.0 KJ/m
Tensile strain	Yield	ISO 527-1	2.3 %
Tensile stress	Yield	ISO 527-1	45.0 MPa
Tensile modulus		ISO 527-1	2200 MPa
Shore hardness		ISO 2039-1	105 MPa
Impact strength of cantilever beam gap	23℃	ISO 180/1A	33.0 KJ/m

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Combustibility	3.20mm	UL 94	HB
Combustibility	Combustibility	1.50mm	UL 94	HB
Vicat softening temperature	B50(50N,50℃/h)	ISO 306	94.0 ℃
Hot deformation temperature	1.80MPa，Unannealed	ISO 75A-1	90.0 ℃
Hot deformation temperature	Hot deformation temperature	0.45MPa，Unannealed	ISO 75B-1	94.0 ℃

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.