Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS M/SHI Schulman Plastics
--
--
Impact modification
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | Schulman Plastics/M/SHI |
|---|---|---|---|
| Melt volume flow rate | 220℃,10kg | ISO 1133 | 10.0 cm |
| density | ISO 1183 | 1.05 g/cm |
| Mechanical properties | Test Condition | Test Method | Schulman Plastics/M/SHI |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-1 | 2.3 % |
| Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eU | No Break KJ/m |
| Tensile modulus | ISO 527-1 | 2200 MPa | |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 33.0 KJ/m |
| Shore hardness | ISO 2039-1 | 105 MPa | |
| Tensile stress | 屈服 | ISO 527-1 | 45.0 MPa |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 27.0 KJ/m |
| -30℃ | ISO 179/1eA | 11.0 KJ/m | |
| Impact strength of simply supported beam without notch | -30℃ | ISO 179/1eU | 93.0 KJ/m |
| Thermal performance | Test Condition | Test Method | Schulman Plastics/M/SHI |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa，未退火，HDT | ISO 75B-1 | 94.0 ℃ |
| 1.80MPa，未退火，HDT | ISO 75A-1 | 90.0 ℃ | |
| combustibility | 3.20mm | UL 94 | HB |
| vicat | B50(50N,50℃/h) | ISO 306 | 94.0 ℃ |
| combustibility | 1.50mm | UL 94 | HB |