HDPE SP 4808 Chandra Asri Petrochemical
0
- کاربردها:Pipeline system
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D1505 | 0.949 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.060 g/10min |
| 190°C/21.6kg | ASTM D1238 | 9.0 g/10min | |
| 190°C/5.0kg | ASTM D1238 | 0.25 g/10min | |
| Environmental stress cracking resistance | 10%Igepal,F50 | ASTM D1693 | >1000 hr |
| Viscosity | 190°C | >100000000 mPa·s |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Hydrostatic Resistance | 12.4MPa:20°C | ISO 1167 | >4.2 day |
| 5.0MPa:80°C | ISO 1167 | >41.7 day | |
| 5.5MPa:80°C | ISO 1167 | >6.9 day | |
| LongitudinalReversion | ISO 2505-1 | 0.63 % | |
| RapidCrackPropagation-S | 0°C | ISO 13477 | >1.20 MPa |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | Yield | ASTM D638 | 30.0 MPa |
| Break | ASTM D638 | 50.0 MPa | |
| elongation | Break | ASTM D638 | >700 % |
| Flexural modulus | ASTM D790 | 1300 MPa | |
| SlowCrackGrowthResistance-NotchTest | 80°C | >1058 hr |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D1822 | 550 kJ/m² |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| brittle temperature | ASTM D746 | <-70.0 °C | |
| Oxygen induction time | 200°C | ASTM D3895 | >80 min |