PP Copolymer SAXALEN™ PPC339T20 SAX AUSTRIA

ویژگی‌ها:
Filler mineral filler 20% filler by weight
مقایسه

برگه داده فنی

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	25.0 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.00 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	4.00 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	55.0 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	24.0 kJ/m²
tensile strength	23°C	ISO 527-2	25.0 MPa
Elongation at Break	23°C	ISO 527-2	18.0 %
Tensile modulus	23°C	ISO 527-2	2400 MPa
bending strength	23°C	ISO 178	33.0 MPa
Bending modulus	23°C	ISO 178	2000 MPa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.00 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.00 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	50.0 kJ/m²

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	70.0 °C
Vicat softening temperature		ISO 306/B50	75.0 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density			1.05 g/cm³
melt mass-flow rate		ISO 1033	12.0 cm³/10min