PAEK K7500CF30 Polymics, Ltd.
0
- ویژگی‌ها:Fillercarbon fiber reinforced material30%filler by weight
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.40 g/cm³ | |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.10 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 23000 MPa | |
| tensile strength | ASTM D638 | 260 MPa | |
| elongation | Break | ASTM D638 | 2.3 % |
| Flexural modulus | ASTM D790 | 24000 MPa | |
| bending strength | ASTM D790 | 386 MPa | |
| compressive strength | ASTM D695 | 258 MPa | |
| coefficient of friction | Dynamic | ASTM D1894 | 0.16 |
| Static | ASTM D1894 | 0.22 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.18mm | ASTM D256 | 60 J/m |
| Suspended wall beam without notch impact strength | 3.18mm | ASTM D256 | 360 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 315 °C |
| Glass Transition Temperature | DSC | 170 °C | |
| melting temperature | DSC | 353 °C | |
| Linear coefficient of thermal expansion | MD：<170°C | ASTM D696 | 1E-05 cm/cm/°C |