PAEK K7500CF30 Polymics, Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Polymics, Ltd./K7500CF30 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.18mm | ASTM D256 | 60 J/m |
| Suspended wall beam without notch impact strength | 3.18mm | ASTM D256 | 360 J/m |
| Mechanical properties | Test Condition | Test Method | Polymics, Ltd./K7500CF30 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 2.3 % |
| tensile strength | ASTM D638 | 260 MPa | |
| compressive strength | ASTM D695 | 258 MPa | |
| Tensile modulus | ASTM D638 | 23000 MPa | |
| Flexural modulus | ASTM D790 | 24000 MPa | |
| coefficient of friction | Dynamic | ASTM D1894 | 0.16 |
| bending strength | ASTM D790 | 386 MPa | |
| coefficient of friction | Static | ASTM D1894 | 0.22 |
| physical property | Test Condition | Test Method | Polymics, Ltd./K7500CF30 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.10 % |
| density | ASTM D792 | 1.40 g/cm³ |
| Thermal performance | Test Condition | Test Method | Polymics, Ltd./K7500CF30 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 315 °C |
| Glass Transition Temperature | DSC | 170 °C | |
| Linear coefficient of thermal expansion | MD：<170°C | ASTM D696 | 1E-05 cm/cm/°C |
| melting temperature | DSC | 353 °C |