LLDPE L2009FA Thailand Siam Chemical

کاربردها:
Bags films industrial applications mixing agricultural applications heavy packaging bags
مقایسه

برگه داده فنی

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
gloss	38.0μm	ASTM D2457	53
turbidity	38.0μm	ASTM D1003	15 %

thermal performance	روش آزمون	نتیجه آزمون
Brittle temperature	ASTM D746	<-70.0 °C
Vicat softening temperature	ASTM D1525	102 °C
Melting temperature	ASTM D2117	122 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D1505	0.919 g/cm³
melt mass-flow rate	190°C/2.16kg	ASTM D1238	1.0 g/10min
Environmental stress cracking resistance	50°C,25%Igepal,Compression Molded,F50	ASTM D1693B	>1000 hr

film	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	TD:Break,38μm	ASTM D882	34.3 MPa
elongation	MD:Break,38μm	ASTM D882	620 %
elongation	elongation	TD:Break,38μm	ASTM D882	840 %
Dart impact	38μm	ASTM D1709	130 g
Elmendorf tear strength	MD:38μm	ASTM D1922	150 g
Elmendorf tear strength	Elmendorf tear strength	TD:38μm	ASTM D1922	370 g
Secant modulus	2%Secant,TD:38μm	ASTM D882	272 MPa
tensile strength	MD:Yield,38μm	ASTM D882	11.8 MPa
	tensile strength	TD:Yield,38μm	ASTM D882	13.7 MPa
	tensile strength	tensile strength	MD:Break,38μm	ASTM D882	37.3 MPa
Secant modulus	2%Secant,MD:38μm	ASTM D882	260 MPa