Plastomer, Ethylene-based Premi-Glas® 1200H-15 USA Premix

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	Compression Molded	ASTM D256	430 J/m
Suspended wall beam without notch impact strength	Compression Molded	ASTM D4812	590 J/m

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Compression Molded	ASTM D638	34.5 MPa
Bending modulus	Compression Molded	ASTM D790	9650 MPa
bending strength	Compression Molded	ASTM D790	96.5 MPa
compressive strength		ASTM D695	145 MPa
Poisson's ratio			0.30
Tensile modulus	Compression Molded	ASTM D638	11700 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	MD3		2.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD4		3.5E-05 cm/cm/°C
thermal conductivity		ASTMC177	0.30 W/m/K
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	130 °C
RTI Str		UL 746	130 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density			1.70to1.85 g/cm³
Shrinkage rate	MD		0.15to0.25 %
Outdoor applicability		UL 746C	f1

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Dielectric strength		ASTM D149	15 kV/mm
Arc resistance		ASTM D495	180 sec