شرایط آزمون | روش آزمون | نتیجه آزمون | |
---|---|---|---|
Tensile strain | Break | ISO 527-2/250 | >300 % |
Shore hardness | 邵氏D,1秒 | ISO 868 | 55 |
brittle temperature | ASTM D746 | <-76.0 °C | |
Dissipation Factor | 50Hz | IEC 60250 | <1.0E-3 |
Degree of crosslinking | 700.0µm7 | 2.0 day | |
700.0µm8 | <25.0 min | ||
1.80mm8 | 1.00 hr | ||
1.80mm7 | 7.0 day | ||
density | ISO 1183 | 0.935 g/cm³ | |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 1.0 g/10min |
Environmental stress cracking resistance | ConditionB,50°C,10%Igepal,F20 | IEC 60811-4-1/B | >96.0 hr |
Carbon black content | ISO 6964 | 2.5 % | |
tensile strength | Yield | ISO 527-2/250 | >15.0 MPa |
Tensile strain | Break | ISO 527-2/250 | >300 % |
brittle temperature | ASTM D746 | <-76.0 °C | |
thermosetting | 200°C3 | IEC 60811-2-1 | 30 % |
200°C4 | IEC 60811-2-1 | 0.0 % | |
ChangeinTensileProperties | 150°C | IEC 60811-1-2 | <25 % |
Tensile Properties Retention | --5 | >85 % | |
--6 | >70 % | ||
Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
dielectric constant | 50Hz | IEC 60250 | <2.90 |
Dissipation Factor | 50Hz | IEC 60250 | <5.0E-4 |
Degree of crosslinking | 23°C,700.0µm7 | 1.5 day | |
23°C,1.80mm7 | 7.0 day | ||
90°C,700.0µm8 | <15.0 min | ||
density | ISO 1183 | 0.923 g/cm³ | |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 1.0 g/10min |
Environmental stress cracking resistance | 50°C,10%Igepal,F20 | IEC 60811-4-1/B | >96.0 hr |
tensile strength | Yield | ISO 527-2/250 | >15.0 MPa |
Tensile strain | Break | ISO 527-2/250 | >300 % |
Shore hardness | 邵氏D,1秒 | ISO 868 | 52 |
brittle temperature | ASTM D746 | <-76.0 °C | |
thermal creep | 200°C3 | IEC 60811-2-1 | 0.0 % |
200°C4 | IEC 60811-2-1 | 60 % | |
Tensile Properties Retention | 135°C5 | IEC 60811-1-2 | >25 % |
Degree of crosslinking | 23°C,1.80mm7 | 7.0 day | |
90°C,700.0µm8 | <15.0 min | ||
90°C,1.80mm8 | 1.00 hr | ||
Change rate of tensile strength in air | 135°C,240hr5 | IEC 60811-1-2 | <25 % |
150°C,168hr6 | IEC 60811-1-2 | <30 % | |
Volume resistivity | IEC 60093 | >1.0E+16 ohms·cm | |
dielectric strength | IEC 60243-1 | >22 kV/mm | |
dielectric constant | 50Hz | IEC 60250 | <2.30 |
Dissipation Factor | 50Hz | IEC 60250 | <5.0E-4 |
Degree of crosslinking | 23°C,700.0µm7 | 1.5 day | |
thermosetting | 200°C3 | IEC 60811-2-1 | 60 % |
200°C4 | IEC 60811-2-1 | 0.0 % | |
Tensile Properties Retention | 150°C6 | IEC 60811-1-2 | >30 % |
Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
dielectric strength | IEC 60243-1 | >22 kV/mm | |
dielectric constant | 50Hz | IEC 60250 | <2.30 |
Dissipation Factor | 50Hz | IEC 60250 | <5.0E-4 |
Degree of crosslinking | 23°C,700.0µm7 | 1.5 day | |
23°C,1.80mm7 | 6.0 day | ||
90°C,700.0µm8 | <15.0 min | ||
90°C,1.80mm8 | 1.00 hr | ||
density | ISO 1183 | 0.930 g/cm³ | |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 1.0 g/10min |
Environmental stress cracking resistance | 50°C,10%Igepal,F20 | IEC 60811-4-1/B | >96.0 hr |
tensile strength | Yield | ISO 527-2/250 | >20.0 MPa |
Degree of crosslinking | 90°C,1.80mm8 | 1.00 hr | |
density | ISO 1183 | 0.923 g/cm³ | |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 1.0 g/10min |
Volume resistivity | IEC 60093 | >1.0E+16 ohms·cm | |
dielectric strength | IEC 60243-1 | >22 kV/mm | |
dielectric constant | 50Hz | IEC 60250 | <2.30 |
Environmental stress cracking resistance | 50°C,10%Igepal,F20 | IEC 60811-4-1/B | >96.0 hr |
tensile strength | Yield | ISO 527-2/250 | >15.0 MPa |
Tensile strain | Break | ISO 527-2/250 | >300 % |
Shore hardness | 邵氏D,1秒 | ISO 868 | 52 |
brittle temperature | ASTM D746 | <-76.0 °C | |
thermosetting | 200°C3 | IEC 60811-2-1 | 60 % |
200°C4 | IEC 60811-2-1 | 0.0 % | |
ChangeinTensileProperties | 135°C5 | IEC 60811-2-1 | <25 % |
150°C6 | IEC 60811-2-1 | <30 % |