PS NORYL™ NH5020 resin

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.11 g/cm³
density	density		ISO 1183	1.11 g/cm³
melt mass-flow rate	280°C/5.0kg	ASTM D1238	9.8 g/10min
Melt volume flow rate	280°C/5.0kg	ISO 1133	10.1 cm³/10min
Shrinkage rate	MD：3.20mm	内部方法	0.50to0.70 %
Water absorption rate	饱和,23°C	ISO 62	0.25 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.050 %

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	0.40mm	UL 94	V-2
	UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	5VA

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Break	ISO 527-2/50	77.5 MPa
elongation	Yield	ASTM D638	5.0 %
Tensile strain	Yield	ISO 527-2/50	4.8 %
elongation	Break	ASTM D638	15 %
Tensile strain	Break	ISO 527-2/50	5.7 %
Flexural modulus	50.0mm跨距	ASTM D790	3000 MPa
Flexural modulus	Flexural modulus		ISO 178	2980 MPa
bending strength		ISO 178	126 MPa
bending strength	bending strength	屈服,50.0mm跨距	ASTM D790	122 MPa
Tensile modulus		ASTM D638	2730 MPa
Tensile modulus	Tensile modulus		ISO 527-2/1	3060 MPa
tensile strength	Yield	ASTM D638	79.2 MPa
	tensile strength	Yield	ISO 527-2/50	80.1 MPa
	tensile strength	tensile strength	Break	ASTM D638	62.2 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C	ASTM D256	91 J/m
	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.1 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.1 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	19.3 J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.9 kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTM D256	59 J/m

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
arc resistance		ASTM D495	PLC6
Compared to the Leakage Tracking Index (CTI)	CTI	UL 746	PLC 2
Compared to the Leakage Tracking Index (CTI)	Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 5
High arc combustion index (HAI)	HAI	UL 746	PLC 0
High Voltage Arc Traceability Rate (HVTR)	PLC	UL 746	PLC 4
Hot wire ignition (HWI)	HWI	UL 746	PLC 0
dielectric strength	3.20mm,在油中	IEC 60243-1	49 kV/mm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
RTI Imp		UL 746	105 °C
RTI Str		UL 746	110 °C
Heat distortion temperature	0.45MPa,未退火,3.20mm，HDT	ASTM D648	122 °C
	Heat distortion temperature	0.45MPa,未退火,6.40mm，HDT	ASTM D648	134 °C
		Heat distortion temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	117 °C
			Heat distortion temperature	1.8MPa,未退火,6.40mm，HDT	ASTM D648	123 °C
			Heat distortion temperature	Heat distortion temperature	1.8MPa,Unannealed,64.0mmSpan，HDT	ISO 75-2/Af	119 °C
vicat		ASTM D152510	138 °C
	vicat	--	ISO 306/B50	138 °C
	vicat	vicat	--	ISO 306/B120	139 °C
ball-indentation hardness	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40到40°C	ASTME831	6.1E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40到40°C	ISO 11359-2	6.1E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40到40°C	ASTME831	6.8E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40到40°C	ISO 11359-2	6.8E-05 cm/cm/°C
RTI Elec		UL 746	110 °C