physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Water absorption rate	23°C,24hr	ASTM D570	0.020to0.060 %
density	--	ASTM D792	0.180to1.35 g/cm³
density	density	23°C	ISO 1183	1.04to1.48 g/cm³
Shrinkage rate	MD:23°C	ASTM D955	0.020to0.31 %
	Shrinkage rate	TD:23°C	ASTM D955	0.29to0.61 %
	Shrinkage rate	Shrinkage rate	23°C	ISO 294-4	0.080to0.70 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	23°C	ASTM D785	105to121

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	23°C	ASTM D638	560to10900 MPa
Tensile modulus	Tensile modulus	23°C	ISO 527-2	4280to14000 MPa
tensile strength	屈服,23°C	ASTM D638	73.5to148 MPa
	tensile strength	屈服,23°C	ISO 527-2	96.1to122 MPa
		tensile strength	断裂,23°C	ASTM D638	97.0to131 MPa
			tensile strength	断裂,23°C	ISO 527-2	82.6to151 MPa
			tensile strength	tensile strength	23°C	ASTM D638	5.00to126 MPa
elongation	断裂,23°C	ASTM D638	1.8to3.0 %
elongation	elongation	断裂,23°C	ISO 527-2	1.7to2.6 %
Flexural modulus	23°C	ASTM D790	3330to9450 MPa
Flexural modulus	Flexural modulus	23°C	ISO 178	3810to11400 MPa
bending strength	23°C	ASTM D790	150to190 MPa
bending strength	bending strength	23°C	ISO 178	108to288 MPa
摩擦系数		ASTM D1894	0.34to0.52

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Suspended wall beam without notch impact strength	23°C	ISO 180	44to66 kJ/m²
Dart impact	23°C	ASTM D3763	1.50to16.3 J
Dart impact	Dart impact	23°C	ISO 6603-2	5.59to13.1 J
Charpy Notched Impact Strength	23°C	ISO 179	12to33 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	39to75 kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	150to300 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	17to29 kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTM D256	740to770 J/m

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
线性热膨胀系数	TD	ISO 11359-2	4.6E-5到8.3E-5 cm/cm/°C
Hot deformation temperature (HDT)	0.45MPa,未退火，HDT	ISO 75-2/B	162to164 °C
	Hot deformation temperature (HDT)	1.8MPa,未退火，HDT	ASTM D648	149to158 °C
		Hot deformation temperature (HDT)	1.8MPa,未退火，HDT	ISO 75-2/A	155to161 °C
		Hot deformation temperature (HDT)	Hot deformation temperature (HDT)	8.0MPa,未退火，HDT	ISO 75-2/C	122to138 °C
vicat		ISO 306	145to166 °C
melting temperature		ISO 11357-3	165to166 °C
线性热膨胀系数	MD	ASTM D696	2.2E-5到6.8E-5 cm/cm/°C
	线性热膨胀系数	MD	ASTME831	1.8E-5到4.7E-5 cm/cm/°C
		线性热膨胀系数	MD	ISO 11359-2	3.3E-5到4.6E-5 cm/cm/°C
		线性热膨胀系数	线性热膨胀系数	TD	ASTME831	4.5E-5到8.3E-5 cm/cm/°C
Hot deformation temperature (HDT)	0.45MPa,未退火，HDT	ASTM D648	158to165 °C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.