Unspecified Generic PP, Unspecified - Glass Fiber, Long Generic
--
--
填料,长玻璃纤维,
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Generic/Generic PP, Unspecified - Glass Fiber, Long |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 12to33 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 44to66 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 150to300 J/m |
| Dart impact | 23°C | ISO 6603-2 | 5.59to13.1 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 17to29 kJ/m² |
| Dart impact | 23°C | ASTM D3763 | 1.50to16.3 J |
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 740to770 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 39to75 kJ/m² |
| hardness | Test Condition | Test Method | Generic/Generic PP, Unspecified - Glass Fiber, Long |
|---|---|---|---|
| Rockwell hardness | 23°C | ASTM D785 | 105to121 |
| Mechanical properties | Test Condition | Test Method | Generic/Generic PP, Unspecified - Glass Fiber, Long |
|---|---|---|---|
| tensile strength | 断裂,23°C | ASTM D638 | 97.0to131 MPa |
| bending strength | 23°C | ASTM D790 | 150to190 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 4280to14000 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 96.1to122 MPa |
| ASTM D1894 | 0.34to0.52 | ||
| elongation | 断裂,23°C | ISO 527-2 | 1.7to2.6 % |
| Flexural modulus | 23°C | ISO 178 | 3810to11400 MPa |
| tensile strength | 23°C | ASTM D638 | 5.00to126 MPa |
| Tensile modulus | 23°C | ASTM D638 | 560to10900 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 82.6to151 MPa |
| Flexural modulus | 23°C | ASTM D790 | 3330to9450 MPa |
| tensile strength | 屈服,23°C | ASTM D638 | 73.5to148 MPa |
| elongation | 断裂,23°C | ASTM D638 | 1.8to3.0 % |
| bending strength | 23°C | ISO 178 | 108to288 MPa |
| physical property | Test Condition | Test Method | Generic/Generic PP, Unspecified - Glass Fiber, Long |
|---|---|---|---|
| Shrinkage rate | 23°C | ISO 294-4 | 0.080to0.70 % |
| density | 23°C | ISO 1183 | 1.04to1.48 g/cm³ |
| Shrinkage rate | MD:23°C | ASTM D955 | 0.020to0.31 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.020to0.060 % |
| density | -- | ASTM D792 | 0.180to1.35 g/cm³ |
| Shrinkage rate | TD:23°C | ASTM D955 | 0.29to0.61 % |
| Thermal performance | Test Condition | Test Method | Generic/Generic PP, Unspecified - Glass Fiber, Long |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 165to166 °C | |
| MD | ASTM D696 | 2.2E-5到6.8E-5 cm/cm/°C | |
| MD | ASTME831 | 1.8E-5到4.7E-5 cm/cm/°C | |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ASTM D648 | 149to158 °C |
| vicat | ISO 306 | 145to166 °C | |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ASTM D648 | 158to165 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 155to161 °C | |
| TD | ISO 11359-2 | 4.6E-5到8.3E-5 cm/cm/°C | |
| TD | ASTME831 | 4.5E-5到8.3E-5 cm/cm/°C | |
| MD | ISO 11359-2 | 3.3E-5到4.6E-5 cm/cm/°C | |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/B | 162to164 °C |
| 8.0MPa,未退火，HDT | ISO 75-2/C | 122to138 °C |