برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.45 g/cm³ |
| Shrinkage rate | TD | | 1.4 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.20 % |
| density | | ISO 1183 | 1.45 g/cm³ |
| Shrinkage rate | TD | | 1.4 % |
| Shrinkage rate | MD | | 1.4 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| water content | | ISO 960 | <800 ppm |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| UL flame retardant rating | 1.60 mm | UL 94 | HB |
| UL flame retardant rating | 3.20 mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ISO 527-2/5 | 3250 MPa |
| tensile strength | 断裂, 23°C | ISO 527-2/5 | 55 MPa |
| Tensile strain | 断裂, 23°C | ISO 527-2/5 | 4.0 % |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 3.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.0 kJ/m² |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 4.0 % |
| Tensile modulus | 23°C | ISO 527-2/5 | 3250 MPa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 55.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 3.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.0 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 70 °C |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 170 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 170 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 70.0 °C |
| vicat | | ISO 306/B | 185 °C |
| melting temperature | | ISO 11357 | 225 °C |
| vicat | | ISO 306/B | 185 °C |
| melting temperature | | ISO 11357 | 225 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.