برگه داده فنی
physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
density | ISO 1183 | 1.58 g/cm³ | |
Shrinkage rate | TD:23°C,2.00mm | ISO 294-4 | 0.90 % |
MD:23°C,2.00mm | ISO 294-4 | 0.40 % | |
Water absorption rate | 23°C,24hr | ISO 62 | 0.50 % |
平衡,23°C,50%RH | ISO 62 | 1.2 % |
flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 750 °C |
Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 675 °C |
1.5mm | IEC 60695-2-12 | 675 °C | |
3.0mm | IEC 60695-2-12 | 960 °C | |
Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 700 °C |
1.5mm | IEC 60695-2-13 | 700 °C | |
UL flame retardant rating | 0.75mm | UL 94 | HB |
1.5mm | UL 94 | HB | |
3.0mm | UL 94 | HB |
Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
Automotive Materials | thicknessd=1mm | FMVSS302 | + |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
Tensile modulus | 23°C | ISO 527-2 | 16800 MPa |
tensile strength | 断裂,23°C | ISO 527-2 | 240 MPa |
Tensile strain | 断裂,23°C | ISO 527-2 | 2.5 % |
Flexural modulus | 23°C | ISO 178 | 16000 MPa |
bending strength | 23°C | ISO 178 | 350 MPa |
Poisson's ratio | ISO 527-2 | 0.40 |
Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 14 kJ/m² |
23°C | ISO 179/1eA | 15 kJ/m² | |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 91 kJ/m² |
23°C | ISO 179/1eU | 95 kJ/m² | |
Impact strength of cantilever beam gap | -30°C | ISO 180 | 16 kJ/m² |
23°C | ISO 180 | 17 kJ/m² |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
Volume resistivity | 0.750mm | IEC 60093 | 1E+12 ohms·cm |
dielectric strength | 1.00mm | IEC 60243 | 20 kV/mm |
arc resistance | 3.00mm | ASTM D495 | PLC 5 |
Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 1 |
High arc combustion index (HAI) | 0.75mm | UL 746 | PLC 0 |
1.5mm | UL 746 | PLC 0 | |
3.0mm | UL 746 | PLC 0 | |
High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
Hot wire ignition (HWI) | 0.75mm | UL 746 | PLC 4 |
1.5mm | UL 746 | PLC 3 | |
3.0mm | UL 746 | PLC 4 |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
Linear coefficient of thermal expansion | MD:23to55°C,2.00mm | ISO 11359-2 | 1.2E-05 cm/cm/°C |
TD:23to55°C,2.00mm | ISO 11359-2 | 1E-04 cm/cm/°C | |
RTI Elec | 0.75mm | UL 746 | 140 °C |
1.5mm | UL 746 | 140 °C | |
3.0mm | UL 746 | 140 °C | |
RTI Imp | 0.75mm | UL 746 | 130 °C |
1.5mm | UL 746 | 130 °C | |
3.0mm | UL 746 | 130 °C | |
RTI Str | 0.75mm | UL 746 | 140 °C |
1.5mm | UL 746 | 140 °C | |
3.0mm | UL 746 | 140 °C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 260 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 255 °C | |
melting temperature | ISO 11357-3 | 260 °C |